Product Range

Aluminium drawn wires
All Aluminium Conductors - AAC
Aluminium Conductors steel reinforced - ACSR
All Aluminium Alloy Conductors - AAAC
Aluminium and aluminium alloy drawn tubes
 

 



Aluminium drawn wires
 
   
  Al wires manufactured from e. conductivity aluminium – Al 99,5%
from diameter 1,6 mm to 11,5 mm.
   
Standards: EN 60889, EN 50183, STN 424004, DIN 48200T5 E-Al
   
Delivered by conditions: Soft STN 424004.11
Semi-hard STN 424004.21
Hard STN 424004.31
   
  Al wires manufactured from aluminium and Al alloys, cold drawn
   
Dimensional standard: STN 427410
Technical and delivery conditions: STN 421418
Packing: steel reels, diameters till 4,5 mm also in rings ( 30-50 kg/ring )
Soft and semi-hard conditions only in rings
   



AAC
All Aluminium Conductor - bare, compressed and sectional
   
  AAC conductors are processed by customers to isulated power cables.
   
Standards: EN 50182, STN 024210, TP 21-95, VDE 0295, GOST 839
DIN 48 201, BS 215
   
Packing: steel reels, wooden drums



ACSR
ACSR conductors are produced from single to max. four layers
   
  Conductors consist from steel core and aluminium outside layer.
   
Standards: EN 50182, PN ZSNP 1/83, STN 024210, ASTM B 232, BS 215
GOST 839, PN-74/E-90083, MSZ 149/4-83
   
Packing: steel reels, wooden drums



AAAC
AAAC conductors are produced from Aluminium alloy AA 6101,
E-AlMgSi 0,5
   
Standard: EN 50182
   
Packing: steel reels, wooden drums


Aluminium drawn tubes
   
Manufactured: Al 99,5% in accordance standard EN 573-3AW 1050A
   
Delivered by conditions: soft H11
medium hard with decreased values H14
medium hard H16
hard H18
   
Produkt range: outer diameter between 6 and 60 mm
  wall thickness from 0,75 to 11 mm
   
Technical conditions for inspection and delivery : EN 734-1
   
Mechanical propertis : EN 754-2
   
Seamless tubes tolerances an dimensions and form EN 754-7

Material standard
EN 573-3 AW 1050A Al 99,5%
Outer diam./wall thickness
6-60mm/0,75-11 mm
Material status
Material Nr.
H11
H14
H16
H18
Temper
soft
medium hard lower values
medium hard
hard
Tensile Strength (MPa)
60-90
100-135
120-160
to wall thickness min. 145
Min. ducility (%)
A5
25
6
4
3
A10
22
5
3
3

 

Aluminium alloy drawn tubes
   
Manufactured: AlMgSi 0,5 standard EN 573-3AW 6060
   
Delivered by conditions: cold hardened, cold formed according to T4
cold formed after solution annealing and hot hardened T6
   
Produkt range: outer diameter between 8 and 40 mm
  wall thickness from 1 do 7 mm

Material standard
EN 573-3 AW 6060 AlMgSi 0,5
Outer diam./wall thickness
8-40mm/1-7 mm
Material status
Material Nr.
T4
T6
Temper
Cold hardened
Cold formed
Cold formed after solution
annealing and hot hardened
Tensile Strength (MPa)
min. 130
min. 215
Min. ducility (%)
A5
15
12
A10
13
10